Microorganisms
Rot
Rot is caused by fungi that grow in the wood and break down the wood’s main building blocks: cellulose, hemicellulose (fibres) and lignin. The colour and shape change considerably and the strength deteriorates.
Wood-decaying fungi need freely available water to grow, which they get if the moisture content exceeds fibre saturation – i.e. around 30 percent. In addition to access to water, nutrients and oxygen, the fungi require an ambient temperature of between 0°C and 40°C in order to grow. Since all four factors are required, the risk of rot disappears if one factor is removed. The water factor is usually the easiest to do something about – for example through structural wood protection, where the wood is protected from long-term moisture absorption. For structures that have an application where this is not possible, such as terraces, the wood can be treated in various ways. This removes the opportunity of the fungi to draw on the nutrients in the wood. See the section on Wood protection.
Blue stain
Blue stain is caused by fungi that grow in and discolour the wood, making it easier for the water to penetrate. It does not, however, affect the strength. The blue stain fungus grows under around the same moisture and temperature conditions (0–40°C) as wood-decaying fungi, but it can grow down to -3°C. At these low temperatures the blue stain fungus is colourless and invisible to the naked eye. The colour appears when the temperature rises to 8–10°C and stays there for a week or so. Pine sapwood is most susceptible to attack, but spruce sapwood is also attacked. Blue stain may, at first sight, look like mould, but can be identified if the wood is also blue beneath the surface. This can be checked by cutting the wood with a knife. Blue stain fungus can establish itself in logs (sap staining), or wood that has been stored improperly (timberyard blue stain), and on a construction site if the wood is not protected from moisture. Blue stain should therefore be avoided in exterior cladding, for example, but its presence is not problematic in encased wood.
Mould
Mould is a fungus that grows on the surface of the wood and can cause surface discolouration. Caused by the mould spores, the discolouration can usually be washed away or planed off and does not affect the strength of the wood, but it could have a negative impact on human health. It is not currently known how or to what extent mould affects human health, but mould should be avoided indoors in buildings where people spend more than just a very short time.
Mould occurs on wood that is stored improperly, for example unprotected during prolonged precipitation, or if it is encased without the opportunity to quickly dry out. Since mould only grows on the surface of the wood, the relative humidity (RH) or the wood’s surface moisture content is the crucial factor in determining where growth occurs.
In contrast to wood-decaying and blue stain fungi, mould is not particularly fussy about where it draws its nutrition from. It is thus not entirely uncommon for mould to also appear on inorganic materials with a soiled surface.
The formation and growth of mould is driven by the RH, the ambient temperature and the length of time that the conditions prevail, as shown in diagram 22. It can therefore be difficult to state a simple RH value when it comes to the risk of mould. At low temperatures, a higher surface moisture content and also a much longer time are required for mould to begin growing. In Sweden, the RH of the outdoor air is high at the time of year when the temperature is low, which explains why wood can be stored outdoors protected against precipitation and ground moisture without major problems.
On the other hand, diagram 22 shows that a rain shower in the summer carries a very high risk of mould growth if the wood is not quickly dried out again. Mould cannot grow at temperatures above 55°C, which explains why no growth occurs in the drying kilns, despite the high moisture content during the first phase of drying.
If wood is to be encased and has been exposed to moisture, it must be dried out before use to prevent mould growth occurring after the wood has been encased. It is recommended that the wood is dried with a construction fan or dehumidifier, for example, until its surface moisture content is no more than 18 percent. If the wood has been exposed to moisture for a long time, so that not only the surface is damp, but also the inner parts of the wood, the moisture content of the wood should also be checked. This is to prevent internal moisture working its way out to the surface after encasing. The moisture content of the wood should be no more than the allowable figures for a target moisture content of 16 percent, with a surface moisture content of max 18 percent. A wood surface that is to be painted should have a surface moisture content of max 16 percent at the time of painting.